四川大学学报（自然科学版）2001，Vol.38Issue(1)：118-121,4.
动态催化聚合C3N4膜的研究
STUDY ON POLYMRIZED C3N4 FILM BY DYAMICSCATALYTIC AGENT METHOD
陈剑瑄 1刘仲阳 1张大忠 1孙官清 1罗伯诚1
作者信息
摘要
Abstract
The C3N4 film on Al2O3 formed by dynamic catalytic at low energy Ar+ ion sputtering C3H6N6 + Ni target. The ratio of nitroge atoms to carbon in the films is 4:3. C(ls) peakes for graphite, diamond and C≡N not have observed, above results are obtained by XPS. The main peak appears at 1275cm- 1 in the Raman spectrum. Resuits of SEM cant observed that sample is consist of cluter type crystal, but is no needle type. The colour is yellow but is no white. The experimental result indicated films consist of inorganic cavalent solid carbon nitride. The results from XRF observed sample contain Fe and Ni elements. It has been illustrated that Fe and Ni responsible for one C3N4 polymerization.关键词