助熔剂对Y2O2S:Ti长余辉磷光体发光性能的影响OA北大核心CSCD
INFLUENCE OFFLLUX ADDITIVES ON THE LUMINESCENT PROPERTIES OF Y2 O2 S:TILONG AFTERGLOW PHOSPHOR
用高温固相还原法合成了无稀土激活离子Y2O2S:0.09Ti长余辉发光材料,研究了Li2CO3,Na2CO3,K2CO3,K3PO4和K2HPO4等5种助熔剂对Y2O2S:Ti磷光体发光性能的影响.结果表明:除了K2HPO4外,加入Li2CO3,Na2CO3, K2CO3与K3PO4助熔剂均可得到单相Y2O2S:Ti晶体.发射光谱结果显示:不同助熔剂的加入并没有改变样品发射谱主峰位置(565 nm),但对其峰强度产生明显影响.助熔剂也显著改善了Y…查看全部>>
A long afterglow phosphor of Y2O2S∶0.09Ti without rare earth activation ion was synthesized by high temperature solid state reduction method. The influence of five fluxes of Li2CO3, Na2CO3, K2CO3, K3PO4 and K2HPO4 on luminescent properties of Y2O2S∶Ti phosphor was investigated. The results indicate that single phase Y2O2S∶Ti could be obtained by adding Li2CO3,Na2CO3, K2CO3 or K3PO4 as flux except K2HPO4 . The emission spectra show that the intensity of emiss…查看全部>>
张朋越;洪樟连;黄秋平;樊先平;王智宇;钱国栋;王民权
浙江大学材料科学与工程系浙江大学材料科学与工程系硅材料国家重点实验室,杭州,310027浙江大学材料科学与工程系浙江大学材料科学与工程系硅材料国家重点实验室,杭州,310027浙江大学材料科学与工程系
化学工程
助熔剂硫氧化钇磷光体发光长余辉
fluxyttrium oxysulfidephosphorluminescencelong afterglow
《硅酸盐学报》 2005 (2)