中国组织工程研究与临床康复2009，Vol.13Issue(8)：1585-1588,4.
两种粘结系统树脂粘结剂机械强度的对比
A comparison study on the mechanical strength of two resin cements
陈海军 1于淑湘 1张林 2钱奇春 1南福清 1林均舟1
作者信息
- 1. 解放军第97医院口腔科,江苏省徐州市221004
- 2. 解放军94592部队医院,江苏省徐州市221005
- 折叠
摘要
Abstract
BACKGROUND: There are many species of ceramic bonding systems supplied in market, the mechanical strength is aprerequisite condition for resin cement in clinical use.OBJECTIVE: To study the difference of mechanical strength between Panavia F resin cement and self-made resin cement,DESIGN, TIME AND SETTING: A controlled observational study was performed in the prosthesis laboratory of the FourthMilitary Medical University of Chinese PLA between May 2006 and March 2007.MATERIALS: Panavia F resin cement was sourced from KURARAY MEDICAL INC. (Japan), experimental resin cement wasproduced by College of Stomatological Medicine in the Fourth Military Medical University of Chinese PLA.METHODS: Five cylindrical compressive strength specimens at an 8-mm height and 4-mm diameter were prepared, as well as5 cylindrical diametral tensile strength specimens at a 3-mm height and 6-mm diameter. AGS-500 universal material testingmachine was applied to detect the compressive strength and diametral tensile strength.MAIN OUTCOME MEASURES: The diametral tensile strength test and compressive strength test of the specimens.RESULTS: The compressive strength of Panavia F resin cement was remarkably higher than that of experimental cement[(238.92±24.54), (149.08±12.13) M Pa, P ＜ 0.05]. There were no significances between two resin cements on diametral tensilestrength (P＞ 0.05).CONCLUSION: There were no significance between two resin cements on diametral tensile strength following completecuring. The compressive strength of experimental resin cement can reach the standard of ADA (＞ 70 MPa) although it is lowerthan the compressive strength of Panavia F resin cement.关键词
树脂粘结剂/径向抗张强度/压缩强度Key words
resin cement/diametral tensile strength/compressive strength分类
医药卫生引用本文复制引用
陈海军,于淑湘,张林,钱奇春,南福清,林均舟..两种粘结系统树脂粘结剂机械强度的对比[J].中国组织工程研究与临床康复,2009,13(8):1585-1588,4.