Defects in aluminum foam with superfine open-cell structure
Defects in aluminum foam with superfine open-cell structure
Wang Fang 1Zhang Zhimin 2Li Baocheng 1Wang Lucai1
作者信息
- 1. College of Material Science and Technology, North University of China, Taiyuan 0300512, China
- 2. College of Material Science and Technology, Taiyuan University of Science and Technology, Taiyuan 030024, China
- 折叠
摘要
Abstract
The infiltration casting process for producing aluminum foam includes three steps: preparing precursor using NaCI particles, infiltrating molten aluminum and cleaning NaCI precursor. Defects occur during the preparation of aluminum foam with superfine open-cell structure, and influence the pore structure and performance of aluminum foam materials. The types of the defect and their forming mechanisms are analyzed in this paper. The defects include point defects and linear metal defects, and are caused by the defects in salt precursor and the insufficient infiltration of molten aluminum into precursor. With the choice of proper precursor preparation method and infiltration process parameters, the complete aluminum foam with superfine pores could be achieved.关键词
aluminum foam/defect/superfine pore/infiltrationKey words
aluminum foam/defect/superfine pore/infiltration分类
矿业与冶金引用本文复制引用
Wang Fang,Zhang Zhimin,Li Baocheng,Wang Lucai..Defects in aluminum foam with superfine open-cell structure[J].中国铸造,2008,5(3):172-174,3.