不同析出状态下Al合金的形变及再结晶织构
Deformation and recrystallization textures of Al alloy with various precipitation states
林丹 1王磊 1陈扬 2宋鸿2
作者信息
- 1. 东北大学
- 2. Liaoning Institute of Technology, Jinzhou 121001, China
- 折叠
摘要
Abstract
The deformation and recrystallization textures of 6111 Al alloy with various precipitation states have been investigated by means of the orientation distribution functions ( ODFs ). It was found that the precipitation state had significant effects on both rolling and recrystallization textures of Al alloy. For the alloy with no or little precipitate, the orientation intensities were distributed more homogeneously along the β-fiber.With increasing aging temperature, the orientation intensities along the β-fiber increased firstly and decreased then. Simultaneity, the orientation intensities along the β-fiber were distributed more and more inhomogeneously. On the other hand, with the precipitates increasing the recrystallization textures changed gradually from {001} <UVW> and very weak {011} <111> orientation to the strong {001} <311> and {011}< 111 > orientation.关键词
Al alloy/texture/deformation/recrystallization/precipitation stateKey words
Al alloy/texture/deformation/recrystallization/precipitation state分类
矿业与冶金引用本文复制引用
林丹,王磊,陈扬,宋鸿..不同析出状态下Al合金的形变及再结晶织构[J].材料与冶金学报,2006,5(4):292-295,4.