人工晶体学报2009，Vol.38Issue(2)：519-524,6.
离子交换树脂均匀沉淀法制备MgO纳米粒子
Preparation of MgO Nanoparticles by Ion Exchange Resin Homogenous Precipitation Method
摘要
Abstract
MgO nanoparticles was prepared by exchange resin homogenous precipitation methods using Mg(NO3)2·6H2O, (NH4)2CO3 and NH3·H2O as raw materials. The MgO nanoparticles was characterized and analyzed by thermo-gravimetric (TC) analysis, infrared (IR) spectrum analysis, X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HR TEM), selected area electron diffraction (SAED) and the bet method (BET). The results indicated that the particles a and b calcined at 700 ℃ had a clear crystal lattice and hexagonal shapes with average 25 nm in diameter, the As with 31 m2/g and 32 m2/g, respectively.关键词
离子交换树脂/均匀沉淀法/MgO纳米粒子/制备Key words
ion exchange resin/homogenous precipitation method/MgO nanoparticles/preparation分类
化学化工引用本文复制引用
刘颖,冯金朝..离子交换树脂均匀沉淀法制备MgO纳米粒子[J].人工晶体学报,2009,38(2):519-524,6.基金项目
The National Natural Science Foundation of China(No. 20767004) （No. 20767004）
the "985 Project" of Minzu University of China (MUC 985-3-3) （MUC 985-3-3）
the "211 Project" of Minzu University of China(MUC 021211306) （MUC 021211306）
the State Key Program of Natural Science Foundation of Inner Mongolia(No.200711020202) （No.200711020202）
Universityies'Science Research Projects of Inner Mongolia(No.NJ06108)) （No.NJ06108）