硅酸盐学报2009，Vol.37Issue(5)：888-891,4.
Nd3+:La2CaB8O16晶体生长及光谱性能
CRYSTAL GROWTH AND SPECTRAL PROPERTIES OF Nd3+:La2CaB8O16
郭锐 1万明 2周浪1
作者信息
- 1. 南昌大学材料科学与工程学院,南昌,330031
- 2. 江西赣江职业技术学院信息学院,南昌,330108
- 折叠
摘要
Abstract
A new neodymium-doped lanthanum calcium borate (Nd3+:La2CaB8O16, Nd:LCB8) polycrystalline powder was synthe- sized, and a Nd:LCB8 single crystal was grown by top-seeded solution growth (TSSG) method with CaB4O7 as flux. X-ray powder diffraction analysis shows that Nd:LCB8 has the same crystal structure as that of LCB8. The melting point of Nd:LCB8 crystal is about 1 046 ℃. The absorption and fluorescence spectra of Nd:LCB8 were measured. There are several absorption bands in the wavelength range of 300-1000 nm due to the 4f3-4f3 transitions of Nd3+ ions in Nd:LCB8 crystal, and the absorption band at 802 nm corresponding to the output wavelengths of AIGaAs diode lasers has a full-width at half-maximum of 19 nm. There are three emission peaks, around 890, 1 060 and 1 330 rim. The measured fluorescence lifetime is about 75 μs at room temperature.关键词
掺钕硼酸钙镧/激光晶体/顶部籽晶法/助溶剂/光谱特性Key words
neodymium-doped lanthanum calcium borate/laser crystal/top-seeded solution growth method/flux/spectral properties引用本文复制引用
郭锐,万明,周浪..Nd3+:La2CaB8O16晶体生长及光谱性能[J].硅酸盐学报,2009,37(5):888-891,4.