镓含量对纯铝的耐蚀性的影响
Studies on the Influence of Gallium Content on the Corrosion Resistance of Pure Aluminum
LIN Jin-ping 1WANG Jun 2SUN Bao-de2
作者信息
- 1. 上海交通大学金属基复合材料国家重点实验室
- 2. The State Key Laboratory of Metal Matrix Composites,Shanghai Jiao Tong University,Shanghai 200240,China
- 折叠
摘要
Abstract
The effect of small amount gallium (up to 0.06%) on the corrosion behavior of pure aluminum (99.99%,4N) in chloride solution was investigated using a potentiodynamic polarization technique.It has been found that the open circuit corrosion potential and the pitting potential shifted in the active (negative) direction with increasing gallium content,while corrosion rate and pitting occurrence factor for aluminum increased.The effect of gallium on the degradation of corrosion resistance is rather small while the gallium content is below 0.03mass%.The gallium content should be kept less than 0.03mass% in the pure aluminum.关键词
Al-Ga alloy/polarization curve/immersion test/pitting corrosionKey words
Al-Ga alloy/polarization curve/immersion test/pitting corrosion分类
通用工业技术引用本文复制引用
LIN Jin-ping,WANG Jun,SUN Bao-de..镓含量对纯铝的耐蚀性的影响[J].材料工程,2008,(z1):90-94,5.