中山大学学报（自然科学版）2009，Vol.48Issue(z2)：92-94,3.
高温黄磷熔渣直接制备微晶玻璃试验研究
Experimental Study on the Direct Preparation of Glass-Ceramic from High Temperature Molten Slag of Yellow Phosphorus
摘要
Abstract
After molten at high temperature in the yellow phosphor furnace, the slag of yellow phosphorus is sent into tundish with sup-plementary materials, and, by nucleating and crystalloid treatment, high-property glass-ceramic is produced. Correlative testing results of glass-ceramic made of the high temperature molten slag of yellow phosphorus reveals that the radioactivity is low and in line with GB; the main crystal phase is wollastonites, ranules of which are thin small, are close and e evenly distribute; the average Micro-hardness sion resistance is much higher than marble's and granite's.关键词
黄磷渣/微晶玻璃/试验Key words