Fabricated and friction test anisotropy material of ultrasonic motor
Fabricated and friction test anisotropy material of ultrasonic motor
QU Yan-yan 1QU Jian-jun 2KUANG Nai-hang3
作者信息
- 1. School of Mechatronics Engineering,Harbin Institute of Technology,Harbin 150001,China
- 2. Harbin FRP Research Institute,Harbin 150001 ,China
- 折叠
摘要
Abstract
The twisters for composed of anisotropic material were designed and manufactured.And two kinds of directional-composites were made:one was fiber direction vertical with frictional interface and another was parallel with frictional interface and moving direction.By varying the proportions of epoxy resin and fiber and arranging the orientations of fiber,the composites anisotropy along longitudinal and circumferential were got.Using density measurement,the mass fraction of resin and fiber were calculated.According to composite mesoscopic mechanics,the elasticity constants of composite were analyzed and calculated.The composite different thicknesses were sliced,and attach to the rotor,then the load characteristics,no-load speed,stop load of ultrasonic motor(USM) were test.The output properties of USM with 0.6 mm thickness composite were superior.The effect of friction material on ultrasonic motor was analyzed.Elastic modulus,thickness and micro-morphology of material are main factors which affect characteristics of ultrasonic motor.关键词
ultrasonic motor/rotor composites/anisotropy/frictionKey words
ultrasonic motor/rotor composites/anisotropy/friction分类
信息技术与安全科学引用本文复制引用
QU Yan-yan,QU Jian-jun,KUANG Nai-hang..Fabricated and friction test anisotropy material of ultrasonic motor[J].哈尔滨工业大学学报（英文版）,2010,17(5):667-671,5.