Research on the Slag Resistance of MgO-C Bricks with Different Matrix
呼伟 1尹洪峰 1史绪波 1刘小团1
作者信息
- 1. 西安建筑科技大学材料科学与工程学院,西安,710055
- 折叠
摘要
Abstract
In order to study the slag resistance of bricks with different matrix , corrosion testing for the crucible samples with three different formulations were made choosing slag A. The microscopic structure of them were observed by scanning electron microscope, energy disperse spectroscopy and X-ray diffraction.The results were that sample 1 concluding fused spinel had the best properties and the best anti-erosion by means of petrographical analysis. Its slag corrosion layer about 20.58 mm thick was the thinnest among the three. Sample 2 and sample 3 concluding calcium magnesium sand had a phenomenon of hydration which is difficult to control and their properties were affected.关键词
镁碳砖/炉渣/侵蚀机理/基质Key words
MgO-C brick/ slag/ erosion mechanism/ matrix分类
化学化工引用本文复制引用
呼伟,尹洪峰,史绪波,刘小团..不同基质结合镁碳砖对炉渣的抗侵蚀性研究[J].硅酸盐通报,2011,30(1):200-204,209,6.