华西口腔医学杂志2011，Vol.29Issue(2)：168-170,3.DOI:10.3969/j.issn.1000-1182.2011.02.016
不同粘接剂对金属烤瓷冠边缘微渗漏影响的研究
A comparative study of marginal microleakage using different cements in porcelain-fused-to-metal crown
摘要
Abstract
Objective To evaluate the marginal microleakage of porcelain-fused-to-metal crown truing four different cement. Methods Sixteen porcelain-fused-to-metal crowns were built and randomly divided into 4 group, luted onto standard prepared human forward molars using four different cements (glass ianomer cement, resin-modified giass ionomer cement, PanaviaF, Super-Bond C&B adhesive luting system). After temperature cycling test, all the crowns were then submerged in 2％ fuchsin for 24 h. The marginal microlenkage at tooth cement interfaces was observed uaing light stereomicroscopy and evaluated in clarification index. The marginal microleakage grade of 4 groups were analyzed by SPSS 13.0. Results The PanaviaF demonstrated the least marginal microleakage, Super-Bond C&B adhesive luting system, resin-medified glass ionomer cement showed an intermediate level of marginal microleakage, glass ionomet cement was aasociated with severe marginal microleakage (total, X2=157.60, P＜0.01; among the different groupa,P＜0.05). Conclusion Adhesive resin luting system which is the first selection in clinical is better than glass ionomer cement and is good at porcelain-fused-to-metal crown.关键词
边缘微渗漏/树脂粘接系统/金属烤瓷冠/染色法/温度循环试验Key words
marginal microleakage/ adhesive resin luting system/ porcelain-fused-to-metal crown: staining method/ temperature cycling test分类
医药卫生引用本文复制引用
姜明欣,黄克强,李志刚,高秀秋,李春山..不同粘接剂对金属烤瓷冠边缘微渗漏影响的研究[J].华西口腔医学杂志,2011,29(2):168-170,3.基金项目
辽宁省教育厅科学研究计划基金资助项目(2008394) （2008394）