银修饰的ZnO纳米线的发光和光响应性质OA北大核心CSCDCSTPCD
Photoluminescence and Photoresponse Property of Ag Modified ZnO Nanowire
采用不同浓度的银溶液对水热方法生长的ZnO纳米线进行了银修饰,并对其形貌、光致发光和光响应特性进行了研究.实验结果表明,随着修饰用银浓度的加大,光致发光的强度减弱.对原生的和用浓度为10mmol/L的银修饰的ZnO纳米线的光响应进行了测试和比较,发现银修饰的ZnO纳米线在380 nm的响应度达4.6 mA/W,其值是未修饰的ZnO纳米线的75倍,说明银修饰有效地提高了ZnO纳米线的光响应特性.
The ZnO nanowires grown via hydrothermal method were modified by Ag with different concentration in solution. The morphology, photoluminescence property, photoresponse of the ZnO nanowire were studied. The results exhibited that the intensity of photoluminescence decreases with the increased Ag concentration. The photoresponses of as-grown and modified by Ag of 10 mmoL/L nanowires were tested and compared.The responsivity of Ag modified ZnO nanowire was 4.6 …查看全部>>
郭亮;赵东旭;张振中;李炳辉;张吉英;申德振
中国科学院,激发态物理重点实验室,长春光学精密机械与物理研究所,吉林,长春,130033中国科学院,研究生院,北京,100039中国科学院,激发态物理重点实验室,长春光学精密机械与物理研究所,吉林,长春,130033中国科学院,激发态物理重点实验室,长春光学精密机械与物理研究所,吉林,长春,130033中国科学院,激发态物理重点实验室,长春光学精密机械与物理研究所,吉林,长春,130033中国科学院,激发态物理重点实验室,长春光学精密机械与物理研究所,吉林,长春,130033
数理科学
ZnO纳米线银修饰光响应
ZnO nanowire Ag modified photoresponse
《发光学报》 2011 (3)
216-219,4
中国科学院知识创新工程重要方向项目(KJCX3.SYW.WOI)资助
评论