压力容器2011，Vol.28Issue(5)：33-40,8.DOI:10.3969/j.issn.1001-4837.2011.05.006
2.25Cr-1Mo-0.25V钢加氢反应器开发与制造中的一些问题
Development of 2.25Cr-1Mo-0.25V Steel Hydrogenater and Some Problems on the Fabrication
摘要
Abstract
The growing demand for increased size of hydrogenators operating at higher process conditions, Vanadium has been added to 2. 25Cr - 1Mo steel to enhance high temperature strength in 80s of 20th century. The addition of Vanadium influences hydrogen trapping, diffusion and stress relaxation, and response to welding and heat treatment. Fabrication procedure must be adjusted to avoid high hardness, low ductility and low rupture stress for weldments. Examples of past problems in 2.25Cr - 1Mo -0.25V steel pressure vessel fabrication and recent research works abroad were briefly introduced. Some suggestions of research program were presented.关键词
2.25Cr-1Mo-0.25V钢/加氢反应器/冷裂纹/再热裂纹/超声检测Key words
2.25Cr-1Mo-0.25V steel/hydrogenator/cold cracking/reheat cracking/ultrasonic examination分类
能源科技引用本文复制引用
柳曾典,陈进,卜华全,陈学东..2.25Cr-1Mo-0.25V钢加氢反应器开发与制造中的一些问题[J].压力容器,2011,28(5):33-40,8.基金项目
本文受863项目(2009AA044802) （2009AA044802）
国际合作项目(2010DFF42960)支持 （2010DFF42960）