合成材料老化与应用2011，Vol.40Issue(2)：23-27,5.
不饱和树脂/炭黑复合材料的制备与性能研究
Research on Preparation and Properties of Unsaturated Polyester Resin/Carbon Black Composite
摘要
Abstract
In this paper, we employed ball milling and ultrasonic irradiation respectively to prepare Unsaturated Polyester Resin/Carbon Black composites. The influences of the two different preparations on the composite properties were studying and comparing. The results showed that the percolation threshold of the composites, which were processed via ball milling or ultrasonic irradiation, were both about 1.8wt％. Tensile strength and elastic modulus of Unsaturated Polyester Resin / Carbon Black composites changed with the carbon black content, when its content was 1 wt％, the two get the maximum. Compared to pure unsaturated polyester resin, composites fabricated by ball milling in the tensile strength and elastic modulus increased by 89％ and 95.8％, while the ultrasonic irradiation mixing enhanced by 23.12％ 38.37％.关键词
炭黑/不饱和树脂/球磨/超声Key words
carbon black/ unsaturated polyester resin/ ball milling/ ultrasonic irradiation分类
化学化工引用本文复制引用
陈幼珠,陈国华..不饱和树脂/炭黑复合材料的制备与性能研究[J].合成材料老化与应用,2011,40(2):23-27,5.基金项目
福建省自然科学基金重点项目(E0820001) （E0820001）