合成材料老化与应用2011，Vol.40Issue(2)：40-46,7.
不同老化模式对光伏背板中PET结晶度的影响
Crystallinity of PET in PhotovoltaicC Backsheet Under Different Ageing Pattern
唐景 1彭丽霞 1张增明 1傅冬华1
作者信息
- 1. 常熟阿特斯阳光电力科技有限公司测试中心,江苏常熟,215562
- 折叠
摘要
Abstract
In this paper, mechanical properties and PET crystallinity of PV backsheet after damp heat ageing,accelerated damp heat ageing and UV irradiation ageing were studied. Relationship between failure of backsheet and crystallinity of PET layer was concluded. The different ageing patterns above were compared. The results show that, in precess of damp heat ageing and accelerated damp heat ageing, PET layer go crystallizing, and crystallinity should be controlled under 38％ for backsheet without failure. In precess of UV irradiation ageing, Molecular structure of PET was destroyed. By comparing the mechanical properties, we found that UV irradiation ageing gave greater influence to PET layer of PV backsheet.关键词
光伏背板/湿热老化/加速湿热老化/紫外辐照/PET结晶度Key words
PV backsheet/ damp heat ageing/ accelerated damp heat ageing/ UV irradiation/ crystallinity of PET分类
建筑与水利引用本文复制引用
唐景,彭丽霞,张增明,傅冬华..不同老化模式对光伏背板中PET结晶度的影响[J].合成材料老化与应用,2011,40(2):40-46,7.