电源技术2009，Vol.33Issue(4)：326-328,3.
SPE水电解池氧电极研究
Study on oxygen electrode of SPE water electrolyzer
任丽彬 1徐志彬 1李勇辉 1易炜 1张军 1刘兴江1
作者信息
- 1. 中国电子科技集团公司,第十八研究所,化学与物理电源技术重点实验室,天津,300381
- 折叠
摘要
Abstract
Oxygen electrode is a dominant electrode of SPE water electrolyzer (WE), of which diffusion layer and catalyst have direct influence on the performance of WE. The titanium oxygen electrode diffusion layers obtained by thermal decomposition, acid immersion, electro-deposition surface modification were evaluated. The effects of oxygen electrode catalyst, temperature, and oxygen electrode diffusion layer on the performance of WE were also discussed. The results showed that the resistance of Ti oxygen electrode diffusion layer decreased after electro-deposition treatment, and did not increase even if it was exposed to the atmosphere for a long time. IrO2-RuO_2 oxygen electrode catalyst has the best catalytic characteristic. Electrolysis voltage decreased increasing temperature. The WE performance was obviously enhanced when electro-deposited Ti mesh was used as oxygen electrode diffusion layer, its current density was more than 1 A/cm~2 at atmosphere pressure,70 ℃, 1.65 V.关键词
固体聚合物电解质/水电解/氧电极Key words
solid polymer electrolyte/ water electrolysis/ oxygen electrode分类
信息技术与安全科学引用本文复制引用
任丽彬,徐志彬,李勇辉,易炜,张军,刘兴江..SPE水电解池氧电极研究[J].电源技术,2009,33(4):326-328,3.