硅酸盐学报2011，Vol.39Issue(8)：1286-1289,4.
ZrB2-SiCpl复合陶瓷的SPS烧结行为及微观结构
SPS Sintering Behavior and Microstructure of ZrB2-SiCpl Composite Ceramics
摘要
Abstract
A zirconium diboride（ZrB2） based composite with silicon carbide platelet（SiCpl） of 15% in volume was prepared by spark plasma sintering（SPS） at 1 600 ℃ for 5 min with pressure and heating rate of 30 MPa and 100 ℃/min,respectively.The densification behavior during sintering,mechanical properties and microstructure of the composites were investigated.Influence of preferred ori-entation of SiCpl on the mechanical properties of the ZrB2–SiCpl composite ceramic was discussed.Results show that the SPS can decrease the sintering temperature of ZrB2 ceramic.Microstructure of the composite with homogeneous and small grains could be obtained,indicating that the rapid sintering can inhibit the abnormal growth of ZrB2 grains.The directional alignment of SiCpl favors the increase of sintering and mechanical properties.关键词
二硼化锆/放电等离子体烧结/碳化硅晶片Key words
zirconium diboride/spark plasma sintering/silicon carbide platelet引用本文复制引用
王明福,汪长安,张幸红..ZrB2-SiCpl复合陶瓷的SPS烧结行为及微观结构[J].硅酸盐学报,2011,39(8):1286-1289,4.基金项目
国防"973"计划(2006CB605207-2)资助项目. （2006CB605207-2）