热塑性丙烯酸树脂对紫外光固化涂料改性研究
MODIFICATION OF UV-CURING COATINGS WITH THERMOPLASTIC ACRYLIC RESIN
摘要
Abstract
The trimethylolpropane tris-acrylate (TMPTA) was modified with thermosplastic acrylicresin for UV-Curing coatings. The methyl methacrylate (A-21) from Rohm and Haas, U. S was best. TMPTA was modified by A-21 at different proportions. The hardness, adhesion, stand wear, stand fire and-humidity, luster, compatibility and corrosion-resistant of the modified resin was measured. 20% of A-21 in the modified resin was the optimum proportion.关键词
热塑性丙烯酸树脂；三羟甲基丙烷三丙烯酸酯(TMPTA)；UV固化改性；甲基丙烯酸甲酯(A-21)Key words
thermosplastic acrylicresin/trimethylolpropane tris-acrylate (TMPTA)/UV-curing coatings/methyl methacrylate (A-21)分类