河北工业科技2011，Vol.28Issue(5)：285-287,3.
X60在硫化氢环境下疲劳裂纹扩展速率研究
Study on fatigue crack growth rate of X60 material in H2S solution
刘庆刚 1郭彦书 1沈士明2
作者信息
- 1. 河北科技大学机械电子工程学院,河北石家庄050018
- 2. 南京工业大学机械与动力学院,江苏南京 210009
- 折叠
摘要
Abstract
Experiments on the fatigue crack growth rate of X60 material in air and in H2S solution were conducted. Because the corrosion fatigue process is very complex and the crack zone is on the welding joint, the data obtained is not perfect. Experiment results show that the fatigue crack growth rate in H2S solution is greater than that in air, and increases with increasing concentration of H2 S solution.关键词
硫化氢/X60/腐蚀疲劳/疲劳裂纹扩展Key words
H2Si X60/ corrosion fatigue/ fatigue crack growth分类
矿业与冶金引用本文复制引用
刘庆刚,郭彦书,沈士明..X60在硫化氢环境下疲劳裂纹扩展速率研究[J].河北工业科技,2011,28(5):285-287,3.