聚苯胺电致变色薄膜的制备及性能
Preparation and Characterization of Polyaniiline Electrochromic Film
摘要
Abstract
Polyaniline (PANI) electrochromic films was made onto commercially available FTO conductive glass substrate by galvanostat method with aniline monomer as raw materials. The effects of aniline concentration, acid species, electrodeposition time and density of the current on the electrochromic properties of the PANI film were studied. The best condition of PANI synthesis was 0.15 mol/L aniline in 1 mol/L H2SO4, current density 10 μA/cm2 for 40 min. The results revealed that the film's coloring efficiency is higher but the layer could cycle only 105 times.关键词