表面技术Issue(5)：73-76,4.
镁合金微弧氧化层上低温化学镀镍研究
Study on Low Temperature Electroless Nickel Plating on the MAO Ceramic Coating of Magnesium Alloy
摘要
Abstract
A low temperature electroless nickel plating process on micro-arc oxidation ceramic coating of magnesium alloy was studied; The component, microstructures, corrosion resistance and wear resistance properties of the plating layer were investigated. The plating solution formula that is suitable for electroless nickel plating on micro-arc oxidation ceramic coating at by 40 V is as follows, NiSO, · 6H2O 40 g/L, NaH2PO2 · H2O 40 g/L, (CH2CH2OH)3 10 mL/L, C6H8O7 · H2O 7. 5 g/L, NH4HF 20 g/L, and pH value of solution keeps by 9. 5 through adding NH3 · H2O. The plating nickel layer formed in the plating solution at 40 ℃ has microcrystalline structure and belongs to low phosphorus plating layer, adheres well on ceramic coating and can seal the holes of ceramic coating. Hence, the plating layer has excellent corrosion resistance and wear resistance properties.关键词
镁合金/微弧氧化预处理/低温化学镀镍Key words
magnesium alloy/micro-arc oxidation/low temperature electroless nickel plating分类
化学化工引用本文复制引用
郭锋,刘向艳,李鹏飞..镁合金微弧氧化层上低温化学镀镍研究[J].表面技术,2011,(5):73-76,4.基金项目
内蒙古自治区自然科学基金项目(2009MS0801) （2009MS0801）
高等学校博士学科点专项科研基金(20091514110003) （20091514110003）