基于废弃混纺纤维的花盆复合材料的成型工艺
Molding Process of Flowerpot Composite Materials Based on Waste Blended Fibers
摘要
Abstract
[Objective] The aim was to study the influence of different process parameters on the mechanical properties of flowerpot composite materials. [ Method] Through taking tensile strength and impact strength as the main indexes, orthogonal experiment and single factor experiment were used to optimize the molding process. [Results] The optimal molding process conditions were as follows: hot pressing temperature was 185℃, hot pressing pressure was 12 Mpa and hot pressing time was 9 min;under these conditions, tensile strength was 68.76 Mpa and impact strength was 9. 13 KJ/m. [ Conclusion] This research provided references for the expanding application of waste fiber composite materials.关键词
混纺纤维/复合材料/成型工艺/拉伸强度/冲击强度Key words
Blended fibers/ Composite materials/ Molding process/ Tensile strength/ Impact strength分类
资源环境引用本文复制引用
王伟,于永玲,吕丽华..基于废弃混纺纤维的花盆复合材料的成型工艺[J].安徽农业科学,2011,39(31):19610-19612,3.基金项目
辽宁省教育厅创新团队项目(2006T027). （2006T027）