SBS改性AH-70沥青乳化前后性能及微观结构研究OA北大核心CSCDCSTPCD
Study on performance and microstructure of SBS modified asphalt AH-70 before and after emulsification
采用先改性后乳化的工艺制备苯乙烯—丁二烯嵌段共聚物(SBS)改性乳化沥青,将其蒸发残留物和改性沥青的性能进行对比,并利用荧光显微镜(FM)、傅里叶红外光谱(Ft-IR)、核磁共振氢谱(1H-NMR)及差示扫描量热(DSC)等分析手段,评价改性沥青乳化前后的微观结构及热稳定性变化.结果表明:改性沥青乳化后的软化点、5℃延度及弹性恢复率均减小,离析试验软化点差变大,性质衰减后仍较基质沥青有大幅度提高,符合I-D级规范要求；改性沥青为两相分散均匀的三维…查看全部>>
The styrene-butadiene block copolymer (SBS) modified asphalt emulsion was prepared by a modification-emulsifi-cation process. The performance of emulsion residue and modified asphalt was analyzed. The microstructure and thermal stability of SBS modified asphalt before and after emulsification were evaluated by means of fluorescence microscope, FT-IR, 1H-NMR and DSC. The results show that compared with modified asphalt, softening point, 5 °C ductility and ela…查看全部>>
张芹芹;范维玉;王铁柱;南国枝
中国石油大学化学工程学院,山东青岛266555中国石油大学化学工程学院,山东青岛266555中国石油大学化学工程学院,山东青岛266555中国石油大学化学工程学院,山东青岛266555
能源科技
SBS改性沥青乳化宏观性质微观结构热稳定性
SBS modified asphalt emulsification macroscopic properties microstructure thermal stability