电池2011，Vol.41Issue(3)：125-128,4.
模压成型工艺制备微晶石墨/树脂双极板
Preparing amorphous graphite/resin bipolar plate by mould pressing process
摘要
Abstract
Amorphous graphite/resin composite bipolar plates for PEMFC were prepared by mould pressing process. Thermoset-ting resin was used as the binder and amorphous graphite as the conductive filler. The effects of filler particle size,filler content, thermosetting resin and moulding condition on the performance of bipolar plates were studied. The bipolar plate prepared with ther-mosetting resin P104-02 whose content was 18% ~ 20% as binder,amorphous graphite whose particle size was 200 ~ 250 mesh as conductive filler,in the moulding condition of 140- 145℃ , 15 - 20 Mpa and 18 ~ 22 min had such performance:flexural strength > 25 Mpa,conductivity > 100 S/cm,permeability < 3 × 10-5 ml/(s·cm2).关键词
质子交换膜燃料电池(PEMFC)/双极板/复合材料/热固性树脂Key words
proton exchange membrane fuel cell(PEMFC)/bipolar plate/composite/thermosetting resin分类
信息技术与安全科学引用本文复制引用
林政宇,张杰,刘兵..模压成型工艺制备微晶石墨/树脂双极板[J].电池,2011,41(3):125-128,4.基金项目
国家“863”计划(2007AA03Z22) （2007AA03Z22）