Mn掺杂对ZnO薄膜结构及发光性能的影响OA北大核心CSCDCSTPCD
Structural and Photoluminescence Analysis of Mn-doped ZnO thin Films
利用脉冲激光沉积的方法在Si衬底上生长出了c轴高度取向的Mn掺杂ZnO薄膜.X射线衍射表明所有样品都具有纤锌矿结构,没有发现其它相,随着掺杂量的增加,c轴晶格常数增大.原子力显微镜结果显示:Mn的掺杂引起了ZnO薄膜表面粗糙度的变化.由光致发光谱发现,在387 nm附近出现了由于近带边自由激子复合引起的紫外峰,还有以430和545 nm为中心的较宽发光峰,结果表明:掺入到ZnO薄膜中的Mn以+2价的价态存在,掺Mn以后的ZnO薄膜带隙变大,…查看全部>>
Zn1-x MnxO thin films were successfully grown on Si (111) substrates by pulsed laser deposition (PLD).X-ray diffraction measurement revealed that all the films were single phase and had wurtzite structure with c-axis orientation.As Mn concentration increased in Zn1-x MnxO films,the c-axis lattice constant increased gradually.Atomic Force Microscopy (AFM) showed that surface roughness and morphology changed with doping concentrations.Photoluminescence spectra…查看全部>>
陈香存;康朝阳;杨远俊;徐彭寿;潘国强
中国科学技术大学,安徽合肥230029中国科学技术大学,安徽合肥230029中国科学技术大学,安徽合肥230029中国科学技术大学,安徽合肥230029中国科学技术大学,安徽合肥230029
数理科学
X射线衍射光致发光ZnO薄膜脉冲激光沉积
X-ray diffraction photoluminescence Mn-doped ZnO thin films PLD
《发光学报》 2011 (12)