航空材料学报2011，Vol.31Issue(6)：68-72,5.DOI:10.3969/j.issn.1005-5053.2011.6.012
单向苎麻纤维增强酚醛树脂复合材料性能的研究
Unidirectional Ramie Fiber Reinforced Composite Based on Phenolic Resin
摘要
Abstract
The unidirectional ramie fiber reinforced composite based on Cycom6070 could be phenolic resin was prepared and the thermal and mechanical properties of resin, fiber and composite were studied. The results show that after cure for lh at 100 °C , the lowest complex viscosity of Cycom6070 resin increase from 0. 1 Pa · S to 3. 6 Pa · S, It could be used to produce prepreg. TGA curve indicates when the temperature increases to 200 °C , the weight loss of ramie fiber is about 8% , and when the temperature is higher than 200 °C , the weight loss curve is sharply declined. Mechanical properties of composite reinforced by unidirectional ramie fiber modified by coupling agent are much higher than those of composite reinforced by ramie fiber without modifying. SEM photographs show that coupling modification increases the compatibility between the resin and fiber in composite.关键词
苎麻纤维/复合材料/偶联处理Key words
ramie fiber/ composite/ coupling modification分类
航空航天引用本文复制引用
刘燕峰,包建文,李艳亮,益小苏..单向苎麻纤维增强酚醛树脂复合材料性能的研究[J].航空材料学报,2011,31(6):68-72,5.基金项目
中国航空工业集团公司创新基金(2010E62116) （2010E62116）