40CrNiMoA钢螺栓断裂原因分析
Fracture Cause Analysis of 40CrNiMoA Steel Bolts
陈昌达1
作者信息
- 1. 贵州黎阳航空发动机公司,安顺561102
- 折叠
摘要
Abstract
Fracture cause of 40CrNiMoA steel bolts was analyzed by means of macroscopic examination, fracture analysis, metallographic examination, hardness testing and chemical composition analysis. The results showed that the fracture mechanism was the hydrogen brittleness fracture, the reason of fracture was due to high absorption content of hydrogen during producing process of the bolts.关键词
40CrNiMoA钢/螺栓/氢脆断裂Key words
40CrNiMoA steel/bolt/hydrogen brittleness fracture分类