Properties of white organic electroluminescent devices based on a new organic metal complex with quantum well structure
摘要
Abstract
A series of white organic electroluminescent devices with a quantum well structure were fabricated based on a new type of organic metal complex bis（2-（4-trifluoromethyl-2-hydroxyphenyl） benzothiazolate） zinc （Zn（4-TfmBTZ）2） by electroplex at NPB/Zn（4-TfmBTZ）2 interface. The results show that the introduction of the hetero-junction quantum well structure can increase effectively the efficiency of electroplex emission, color rendering index（CRI）,and the color coordination stability. The optimized device ITO/NPB （60 nm）/Zn（4-TfmBTZ）2（3.0 nm）/NPB （4.0 nm） /Zn（4-TfmBTZ）2（30 nm） /Alq3 （30 nm）/LiF（1.5 nm）/Al（150 nm） is obtained with color coordinates of （0.324, 0.337）, the highest CRI of 92.5, a maximal brightness of 2013 cd/m2, and a maximal efficiency of 1.03 cd/A,. This device shows very high color stability when the driving voltage is varied from 10 V to 14 V.关键词
二（2-（4-三氟甲基-2-羟基苯基）苯并噻唑锌/电致激基复合物/量子阱/白光Key words
bis（2-（4-trifluoromethyl-2-hydroxyphenyl） benzothiazolate） zinc/electroplex/white light分类
信息技术与安全科学引用本文复制引用
孟维欣,郝玉英,许慧侠,王华,刘旭光,许并社..基于一种新型有机金属配合物的量子阱结构有机电致白光器件的性能研究[J].物理学报,2011,60(9):675-679,5.基金项目
国家自然科学基金 （）
教育部长江学者与创新团队发展计划项目 （）
山西省自然科学基金（批准号：2008011008 2010021023-2）资助的课题 （）