钴离子注入对二氧化钛晶体的结构和光学性能的影响
Effect of Co~＋ implantation on structural and optical properties in single-crystal TiO_2
摘要
Abstract
Ion implantation technique is used for doping Co＋to single crystal TiO2（001）.The implanted energies and the fluences of Co＋ are 40keV and 1×1016cm-2;80 keV and 5×1015,1×1016,5×1016,1×1017cm-2;120 keV and 1×1016cm-2,respectively.And then,the structural and the optical properties of all samples are characterized by using X-ray photoelectron spectroscopy （XPS）,X-ray powder diffraction （XRD）,UV - Vis diffuse reflectance spectroscopy （UV-Vis DRS）,and these impurities in implanted samples are also analyzed.From the XRD spectra of implanted samples we observe that the greater damage is caused with the increase of the kinetic energy of incident ions.UV - Vis diffuse reflectance spectroscopy measurement shows that the absorbance of visible band is enhanced in all the implanted samples,and the optical band gap decreases with implanted ion fluence increasing from 5×1015cm-2 to 5×1016cm-2.关键词
钴/二氧化钛/离子注入/掺杂Key words
Co/TiO2/ion implantation/doped分类
化学化工引用本文复制引用
李天晶,李公平,马俊平,高行新..钴离子注入对二氧化钛晶体的结构和光学性能的影响[J].物理学报,2011,60(11):484-488,5.基金项目
兰州大学磁学与磁性材料教育部重点实验室开放课题 （）
兰州大学中央高校基本科研业务费专项基金（批准号：860452）资助的课题山东大学晶体材料国家重点实验室基金 （）
教育部春晖计划（批准号：Z2008-1-62023）、教育部留学回国人员科研启动基金 （）