Effect of cooling rate on MC carbide in directionally solidified nickel-based superalloy under high thermal gradient

Zhang Weiguo Liu Lin Fu Hengzhi

中国铸造2012，Vol.9Issue(1)：11-14,4.

Effect of cooling rate on MC carbide in directionally solidified nickel-based superalloy under high thermal gradient

Zhang Weiguo ¹Liu Lin ²Fu Hengzhi²

作者信息

1. College of Mechanical & Electronic Engineering, Northwest A & F University, Yangling 712100, China
2. State Key Laboratoryof Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China
折叠

摘要

关键词

directional solidification/cooling rate/nickel-based superalloy/MC carbide

Key words

directional solidification/cooling rate/nickel-based superalloy/MC carbide

分类

矿业与冶金

引用本文复制引用

Zhang Weiguo,Liu Lin,Fu Hengzhi..Effect of cooling rate on MC carbide in directionally solidified nickel-based superalloy under high thermal gradient[J].中国铸造,2012,9(1):11-14,4.

基金项目

This study was financially supported by the Scientific Research Foundation for Ph.D.,Northwest A & F University (No.Z109021103) （No.Z109021103）

the Special Fund for Basic Scientific Research of Central Colleges,Northwest A & F University No.Z109021114) and the fund of the State Key Laboratory of Solidification Processing in NWPU (SKLSP201220). （SKLSP201220）

中国铸造

OASCI

ISSN：1672-6421

访问量0

下载量0

段落导航