冷却速率对奥氏体不锈钢凝固过程影响的原位观察OA北大核心CSCDCSTPCD
Effect of cooling rate on the solidification process of austenitic stainless steel by in-situ observation
通过采用激光共聚焦扫描显微镜对AISI304奥氏体不锈钢的凝固过程进行了原位动态观察研究.发现当冷却速率为0.05℃.s-1时,奥氏体不锈钢以胞状晶方式凝固,其凝固模式为FA模式,即δ铁素体相先从液相中形核并长大,γ相在1 448.9℃时通过与液相发生包晶反应（L＋δ→γ）在δ铁素体相界形成,当温度降到1 431.3℃时液相消失,δ铁素体相通过固态相变转变为γ相,富Cr贫Ni的残留铁素体位于胞状晶之间.当冷却速率为3.0℃.s-1时,奥氏体不锈钢…查看全部>>
Solidification processes of AISI304 austenitic stainless steel at cooling rates of 0.05℃.s-1 and 3.0 ℃.s-1 were observed in situ by confocal laser scanning microscopy. When the cooling rate is 0. 05 ℃.s-1 the solidification front is cellular morphology and the solidification mode belongs to FA mode. B ferrite appears firstly in liquid steel, and then γ phase precipitates prior at B-grain boundaries at 1 448.9℃ by means of the periteetic reaction （L＋δ→γ）. At …查看全部>>
黄福祥;王新华;王万军
北京科技大学冶金与生态工程学院,北京100083／北京科技大学材料科学与工程学院,北京100083北京科技大学冶金与生态工程学院,北京100083北京科技大学冶金与生态工程学院,北京100083
冶金工业
连铸奥氏体不锈钢凝固微观结构相变共聚焦显微镜
continuous castingaustenitic stainless steelsolidificationmicrostructurephase transitionsconfoeal microscopy
《北京科技大学学报》 2012 (5)