电磁改性T-ZnOw的制备及性能研究
Electromagnetic Modification of T-ZnOw and It's Performance
摘要
Abstract
The T-Zn()w was modified by the chemical deposition method. The modified sample was characterized by XRD, SEM and EDX. The results show that there are cubic system metal iron and hexagonal wurtzite ZnO in the sample. The modified sample really keeps the intact tetrapod structure and its surface is coated fully by spherical iron particles about 0. 5fjim in diameter. The weight fraction of iron element and zinc element in the modified sample are 63% and 37% respectively. Saturation magnetization and resistivity of the modified sample are 85. 66 emu/g and 6. 9 D, ? Cm, respectively.关键词
电磁改性/化学沉积法/T-ZnOwKey words
electromagnetic modification/ chemical deposition/ T-ZnOw分类