潜伏性环氧固化剂的制备及其水性环氧涂料的性能研究
Preparation of Latent Curing Agent and the Performance of Its Water-based Epoxy Coating
摘要
Abstract
A kind of latent curing agent for waterborne epoxy was synthesized using bisphenol A , formal-dehyde and dicyandiamide as monomers. The curing properties of the latent curing agent/epoxy E-51 were characterized by DTA. The stability and film property of the prepared water-borne epoxy emulsion were studied. Results show that the optimal content of curing agent is 45% and the curing temperature is 150 "C when epoxy resin was cured with the synthesized latent curing agent. The particle size of the water-based epoxy resin emulsion is about 0. 38 ;im and won't de-laminated at 3 000 r/min centrifugation for 30 min and has a storage period up to 6 months. Its cured paints have good film properties.关键词
水性环氧树脂/潜伏性固化剂/双氰胺/改性/储存期Key words
waterborne epoxy/ latent curing agent/ dicyandiamide/ modification/ storage period分类
化学化工引用本文复制引用
周建萍,赵海芳,刘志雷,曾庆煜..潜伏性环氧固化剂的制备及其水性环氧涂料的性能研究[J].表面技术,2012,41(2):105-108,4.基金项目
江西省材料中心资助项目(2008AZ1013) （2008AZ1013）
江西省教育厅资助项目(GJJ10509) （GJJ10509）