表面技术2012，Vol.41Issue(3)：100-104,5.
铝上氨基磺酸盐镀铁取代镍中间层的工艺研究
Study on Sulphamate Iron Plating on Aluminum Substrate as Nickle Substitute
王洺浩 1周超亮 2谢磊 2胡晋 2李宁1
作者信息
- 1. 哈尔滨工业大学化工学院,哈尔滨150001
- 2. 无锡新大中薄板有限公司,无锡214183
- 折叠
摘要
Abstract
Aiming at lowering the cost and reducing the pollution in solderable electroplating process of aluminum substratei the technology of iron plating in ferrous sulphamate bath system as nickle substitute after zincation process was achieved. Technical conditions such as bath Ph* operating temperature and bath compositions were optimized through Hull cell test. The adhesion, corrosion behavior and solderability of the corresponding coatings acquired in the optimum conditions were characterized respectively. It indicates that sulphamate iron plating technology could achieve well coating adhesion and solder wetting ability of tin-plating layer though the anti-corrosion behavior is not so good.关键词
铝/电镀铁/氨基磺酸盐/代镍镀层/可焊性Key words
aluminum/ iron plating/ sulphamate/ nickle substitute/ solderability分类
化学化工引用本文复制引用
王洺浩,周超亮,谢磊,胡晋,李宁..铝上氨基磺酸盐镀铁取代镍中间层的工艺研究[J].表面技术,2012,41(3):100-104,5.