Effects of Withdrawing Rate on Low Cycle Fatigue Properties of Single Crystal Superalloy DD6 at 650℃

中文摘要英文摘要

采用2mm/min,4.5mm/min和7mm/min的抽拉速率制备了DD6单晶高温合金试棒.研究了抽拉速率对合金650℃低周疲劳性能的影响.利用扫描电镜(SEM)和透射电镜(TEM)分析了疲劳试样的断口形貌和微观组织.研究结果表明:随抽拉速率的增大,γ’相尺寸减小,一次枝晶间距差异不大,二次枝晶呈发达的趋势.抽拉速率4.5 mm/min的合金650℃低周疲劳寿命最长.DD6合金表现为基本稳定的循环应力响应行为.疲劳裂纹主要萌生于试样亚表面,随应…查看全部>>

The bars of single crystal superalloy DD6 were prepared with withdrawing rates of 2mm/min, 4.5mm/min, 7mm/min. The low cycle fatigue properties of alloy with different with drawing rates were studied comprehensively at 650℃. The fatigue fracture morphology and microstructure were investigated using SEM and TEM. The results show that with the increasing of withdrawing rate, the size of γ' precipitates decreases and quadratic dendrite arm spacing developed gra…查看全部>>

刘维维;唐定中;李嘉荣;刘世忠;熊继春

北京航空材料研究院先进高温结构材料重点实验室,北京100095北京航空材料研究院先进高温结构材料重点实验室,北京100095北京航空材料研究院先进高温结构材料重点实验室,北京100095北京航空材料研究院先进高温结构材料重点实验室,北京100095北京航空材料研究院先进高温结构材料重点实验室,北京100095

金属材料

DD6单晶高温合金抽拉速率低周疲劳

DD6 single crystal superalloy withdrawing rate low cycle fatigue

《航空材料学报》 2012 (2)

8-12,5

10.3969/j.issn.1005-5053.2012.2.002

评论

您当前未登录!去登录点击加载更多...