芳纶阻燃粘胶玻璃纤维包芯纱织物耐热性分析
Heat Resistance Analyses of Aramid1313 Flame Retardant Viscose Glass Fiber Core Spun Yarn Fabric
摘要
Abstract
Heat resistance of aramid 1313 flame retardant viscose glass fiber core spun yarn fabric was studied. Heat loss rate,fabric mechanical property and performance characteristics of the fabric were tested in different heat treatment temperature and time. The result shows that the fabric heat loss rate is increased as the treat time and temperature increase, decline of the fabric mechanical property is not declined significantly, the fabric dimensional stability and shape retention are better. It is considered that the fabric can be used in 250 ℃ for a short time and can be used in 200 ℃ for a long time.关键词