热轧温度对Zr-4合金力学性能和耐腐蚀性能的影响
The effect of hot rolling temperature on the mechanical property and the corrosion resistant property of Zircaloy-4 alloy
李麦海 1武宇 1姚修楠1
作者信息
- 1. 西部金属材料股份有限公司,陕西西安710065
- 折叠
摘要
Abstract
The process of hot rolling has important effects on the mechanical property and the corrosion resistant property of Zircaloy-4 alloy.The Zircaloy-4 plates of 2.4 mm thickness were prepared at different hot rolling temperature of 800 ℃ and 960 ℃,and after the same process of annealing and cold rolling,the Zircaloy-4 plates of 1.2 mm thickness and 0.6 mm thickness were prepared.The effect of hot rolling temperature on the mechanical property and the corrosion resistant property of Zircaloy-4 plates were investigated.The results indicate that the mechanical strength of Zircaloy-4 alloy plates which were prepared at the hot rolling temperature of 800 ℃ is inferior to that prepared at the hot rolling temperature of 960 ℃,and the elongation is superior to that prepared at the hot rolling temperature of 960 ℃.The corrosion resistant property of the plates of 6 mm thickness prepared at the hot rolling temperature of 800 ℃ is superior to that prepared at the hot rolling temperature of 960 ℃.The results also indicate that hot rolling temperature should be controlled reasonably in practical production process.关键词
锆合金/热轧温度/力学性能/耐腐蚀性能Key words
zirconium alloy/hot rolling temperature/mechanical property/corrosion resistant property分类
矿业与冶金引用本文复制引用
李麦海,武宇,姚修楠..热轧温度对Zr-4合金力学性能和耐腐蚀性能的影响[J].宁夏工程技术,2012,11(1):54-55,2.