还原-氧化预处理对双孔道钴基催化剂催化性能的影响OA北大核心CSCDCSTPCD
Influence of reduction-oxidation pretreatment on the performance of bi-modal structure Co-based catalysts in Fischer-Tropsch synthesis
以双介孔分布MCM-41分子筛为载体,采用等体积浸渍法制备了钴基催化剂,并考察了还原-氧化预处理方式对催化剂结构及费托合成催化性能的影响.新鲜催化剂经预处理之后,XRD结果显示钴物种主要以单质钴形式存在,且主要以面心立方钴晶型出现,晶粒粒径由原来的8.4nm增加到22.6nm,由于晶粒粒径的增大,拉曼峰呈现蓝移特征.SEM及TEM表征表明,预处理后催化剂中钴物种在载体中有较好的分散性.H2 -TPR结果表明,新鲜催化剂经还原-氧化预处理后钴物种的…查看全部>>
Co-based catalyst supported on bi-modal MCM-41 molecular sieves was prepared by incipient-wetness impregnation method; the influence of reduction and oxidation pretreatment on the catalyst structure and its performance in Fischer-Tropsch synthesis (FTS) was investigated. XRD results showed that the cobalt species in the catalyst after the pretreatment is in me form of metal cobalt with face centered cubic crystal phase and the crystallite size is increased f…查看全部>>
王俊刚;李德宝;黄巍;贾丽涛;孙志强;刘斌;孙予罕
中国科学院山西煤炭化学研究所煤转化国家重点实验室,山西太原030001中国科学院研究生院,北京100049中国科学院山西煤炭化学研究所煤转化国家重点实验室,山西太原030001潞安(矿业)集团有限公司,山西长治046204中国科学院山西煤炭化学研究所煤转化国家重点实验室,山西太原030001山西潞安煤基合成油有限公司,山西屯留046100山西潞安煤基合成油有限公司,山西屯留046100
化学
双孔道MCM-41分子筛预处理钴基催化剂费-托合成
bi-modal structure MCM41 Co-based catalyst pretreatment Fischer-Tropsch synthesis
《燃料化学学报》 2012 (4)
介孔碳负载的钴基催化剂设计及其费托反应性能的研究
441-446,6
国家自然科学基金(21076218,21003149)
评论