有序介孔碳负载NiCo2O4电极的制备及其超电容性能OA北大核心CSCDCSTPCD
Preparation of Ordered Mesoporous CarbonlNiCo2O4 Electrode and Its Electrochemical Capacitive Behavior
以有序介孔碳(OMC)为载体,采用共沉淀法制备了OMC/NiCo2O4复合物.用X射线衍射(XRD)、傅里叶变换红外(FT-IR)光谱和透射电镜(TEM)研究其结构与形貌,发现NiCo2O4纳米颗粒均匀地负载在有序介孔碳上.循环伏安和恒流充放电测试表明,NiCo2O4质量分数为40％时,在1 A·g-1的电流密度下,复合物电极的比电容可以达到577.0 F·g-1,电流密度为8A·g-1时,比电容可以达到470.8 F·g-1,并具有良好的…查看全部>>
OMC/NiCo2O4 composite was prepared by co-precipitation with ordered mesoporous carbon (OMC) as a support. The crystalline structure and morphology of the composite were investigated by X-ray diffraction (XRD), Fourier-transform infrared (FT-IR) spectroscopy, and transmission electron microscopy (TEM). TEM images showed that NiCo2O4 was uniformly coated on the OMC. Cyclic voltammetry and galvanostatic charge-discharge were used to investigate the electrochemi…查看全部>>
车倩;张方;张校刚;卢向军;丁兵;朱佳佳
南京航空航天大学材料科学与技术学院,南京210016南京航空航天大学材料科学与技术学院,南京210016南京航空航天大学材料科学与技术学院,南京210016南京航空航天大学材料科学与技术学院,南京210016南京航空航天大学材料科学与技术学院,南京210016南京航空航天大学材料科学与技术学院,南京210016
化学化工
超级电容器有序介孔碳NiCo2O4共沉淀法
Supercapacitor Ordered mesoporous carbon NiCo2O4 Co-precipitation method
《物理化学学报》 2012 (4)
837-842,6