Preparation and Electrochemical Performance of TiO2/GNs Nanocomposite as Anode Materials for Lithium-Ion Batteries

中文摘要英文摘要

采用无表面活性剂回流法制备了蜂窝状TiO2/石墨烯(GNs)复合材料.扫描电子显微镜(SEM)及透射电子显微镜(TEM)表征结果表明,TiO2颗粒约5~10 nm,均匀地分散在石墨烯的表面.锂电池测试显示,1C充电容量稳定在240.1 mAh.g-1;30C充电容量为169.5 mAh.g-1;当电流调回1C时,其充电容量仍可完全恢复(241.7 mAh.g-1);10C 300周期循环电极容量保持率为89.8%.

The honeycomb-like porous TiOJgraphenes (TiOJGNs) nanocomposite was prepared by a reflux method. SEM and TEM results showed that nanosized anatase TiO2 (about 5 - 10 nm) were dispersed uniformly on the surface of the GNs. The TiO2/GNs composite showed excellent rate and cycling performance. A stable charge capacity of 169.5 mAh g-1 was obtained at 30C, and can restore to 241.7 mAh g-1 while current went back to 1C. The stable charge capacity of TiOJG…查看全部>>

秦琳琳;张焕;刘晓静;许剑辉;施一宁;郑明森;董全峰

厦门大学固体表面物理化学国家重点实验室,化学化工学院化学系,福建厦门361005厦门大学固体表面物理化学国家重点实验室,化学化工学院化学系,福建厦门361005厦门大学固体表面物理化学国家重点实验室,化学化工学院化学系,福建厦门361005厦门大学固体表面物理化学国家重点实验室,化学化工学院化学系,福建厦门361005厦门大学固体表面物理化学国家重点实验室,化学化工学院化学系,福建厦门361005厦门大学固体表面物理化学国家重点实验室,化学化工学院化学系,福建厦门361005厦门大学固体表面物理化学国家重点实验室,化学化工学院化学系,福建厦门361005

化学化工

锂离子电池负极材料TiO2石墨烯

lithium-ion batteryanode materialsTiO2graphene

《电化学》 2012 (3)

201-204,4

国家自然科学基金项目(No.200933005,No.02903077)国家973项目(No.2009CB220102)资助厦门市纯电动汽车重大科技专项(I期)(No.3502Z20121002)

评论

您当前未登录!去登录点击加载更多...