SnO2∶Sb/SiO2复合薄膜的制备与光学性能OA北大核心CSCDCSTPCD
Preparation and Optical Properties of SnO2∶ Sb/SiO2 Composite Film
采用溶胶-凝胶结合旋涂技术在玻璃基底上制备了SnO2∶Sb/SiO2复合薄膜,利用XRD、FT-IR、SEM、椭偏仪、分光光度计等方法对薄膜样品进行了系统地表征.结果表明:经过热处理后样品生成了SnO2∶Sb和SiO2∶薄膜具有双层结构,上层SiO2厚度约105nm,折射率为1.352,底层SnO2∶Sb厚度约1200 nm,折射率为1.91；优化工艺条件下SnO2∶ Sb/SiO2复合薄膜的性能优于SnO2∶ Sb薄膜,在相同情况下SnO2∶ …查看全部>>
SnO2 : Sb/SiO2 composite films were coated onto glass substrates by sol-gel method. The samples were characterized by X-ray diffraction ( XRD) , fourier transform infrared spectroscopy ( FT-IR), scanning electron microscope (SEM), ellipsometer and spectrophotometer. The results showed that the composite film is composed of SnO2: Sb and SiO2 two kinds of oxide after annealed in air. The SEM images of the samples showed that two-layer structure can be observed…查看全部>>
王贺;魏长平;彭春佳;程果;李丛昱
长春理工大学化学与环境工程学院,长春130022长春理工大学化学与环境工程学院,长春130022长春理工大学化学与环境工程学院,长春130022长春理工大学化学与环境工程学院,长春130022长春理工大学化学与环境工程学院,长春130022
数理科学
溶胶-凝胶SnO2∶SbSiO2复合薄膜透过率
sol-gel SnO2: Sb SiO2 composite film transmittance
《硅酸盐通报》 2012 (3)
683-687,5
评论