退火对聚碳酸酯注塑制品力学及动态力学性能的影响OA北大核心CSCDCSTPCD
Effect of annealing on mechanical and dynamic mechanical properties of polycarbonate injection molding product
研究了聚碳酸酯注塑制品退火后的力学及动态力学性能的变化.结果表明,制品的应力集中情况有明显改善,力学性能除断裂伸长率外都产生了较高提升,拉伸强度提高了14.86％,弯曲强度提高了12.7％,弯曲模量提高了21.27％,冲击强度提高了17.93％;动态力学分析结果表明,注塑制品的内部存在应力.经退火后,注塑制品内部取向、缠结的分子链得到充分松弛,制品储能模量随温度的变化呈线性规律,内部链段的状态稳定,热变形温度得到了提高.而未退火试样的储能模量随温…查看全部>>
The effect of annealing on the mechanical and dynamic mechanical properties of injection mold polycarbonate part was investigated. The results revealed that the residual stress of the polycarbonate injection products tended to reduce due to rearrangement of orientation molecular chains by annealing. Mechanical properties of the products were improved except breaking elongation, with yield strength increased by 14.86%, flexural strength by 12.7%, flexural mod…查看全部>>
张勤星;李倩;张果;王利霞;申长雨;张响
郑州大学橡塑模具国家工程研究中心,河南郑州450002郑州大学橡塑模具国家工程研究中心,河南郑州450002郑州大学橡塑模具国家工程研究中心,河南郑州450002郑州大学橡塑模具国家工程研究中心,河南郑州450002郑州大学橡塑模具国家工程研究中心,河南郑州450002郑州大学橡塑模具国家工程研究中心,河南郑州450002
化学化工
退火力学性能动态力学性能
annealing mechanical property dynamic mechanical property
《化工学报》 2012 (6)
1929-1933,5