Effect of discrete distribution of powder size on magnetic properties of NdFeB
制备了一种NdFeB永磁材料,探讨了制粉前处理方式对粉末离散性、粒径及成品NdFeB永磁体结构与性能的影响.原材料经熔炼、粗破碎后,采用高速风选和高压氢爆2种制粉前处理方式,然后采用同样的成型、烧结和回火工艺制备得到(PrNd)32.3Nb0.70Al0.60Cu0.20B1.03Fe65.12合金,并系统研究了该合金的显微结构和磁性能.结果表明:高压氢爆处理后得到的粉末粒度呈单分散性,粉末粒径较细,所制备得到的磁体样品的微观结构均匀性也较好；高…查看全部>>
(PrNd)32.3Nb0.70Al0.60Cu0.20B1.03Fe85.12 (weight percent) alloys were prepared via different powdering processes, i. e. air classification AC) and hydrogenation decomposition(HD). Their microstrutures and magnetic properties were investigated. The results show that, HD produces monodispersed fine powders, with which the magnets prepared have uniform micro-structure. Moreover, the maximum magnetic energy product, remanence and intrinsic coercivity of the magn…查看全部>>
蒋宏彬;肖李鹏;魏成富;唐杰;张林;赵导文;邓盛贤
绵阳师范学院物理与电子工程学院,四川绵阳621000中国工程物理研究院机械制造工艺研究所,四川绵阳621900绵阳师范学院物理与电子工程学院,四川绵阳621000绵阳师范学院物理与电子工程学院,四川绵阳621000中国工程物理研究院激光聚变研究中心,四川绵阳621900中国工程物理研究院激光聚变研究中心,四川绵阳621900绵阳西磁磁电公司,四川绵阳621000
矿业与冶金
NdFeB磁体离散分布微观结构风选氢爆
NdFeB magnetsdiscrete distributionmicrostructure air classificationhydrogenation decomposition