新型炭材料2012，Vol.27Issue(3)：233-240,8.
塑料用C364色素炭黑的结构与性能
C364 carbon black pigment as a reinforcement in plastics
摘要
Abstract
Three samples, C364 carbon black, C364 carbon black pigment after a two step ozone oxidation, and MA 100 from Mitsubishi Corporation, were characterized by XPS, IR, SEM, PY-GC/MS spectroscopy and elemental analysis. The processing parameters, mechanical properties, aging resistance and micro-morphology of the oxidized C364 carbon black pigment and its composites with polyethylene, polyvinyl chloride and poly(acry-lonitrile-butadiene-styrene) resins were characterized by a HAAKE torque rheometer, scanning electron microscopy and an aging test chamber. Results show that oxidized C364 carbon black pigment contains more hydroxyl, carbonyl, carboxyl and other functional groups than the original C364 sample. The mechanical properties of the composites with oxidized C364 carbon black pigment were almost the same as those of MAlOO-based ones. Oxidation of the C364 carbon black pigment significantly increased the photo aging lifetime of the polyethylene-based composite 10 times.关键词
C364/色素炭黑/塑料/微观结构/性能Key words
C364/ Carbon black/ Plastic/ Microstructure/ Property分类
化学化工引用本文复制引用
徐艳莲,陈钦慧,胡炳环,林金火,夏建荣,陈智贤,黄鹏飞,俞国庆,陈敏辉..塑料用C364色素炭黑的结构与性能[J].新型炭材料,2012,27(3):233-240,8.基金项目
国家自然科学基金(51073037),福建省自然科学基金(2010J01030),福建省科技计划项目(2005H085). （51073037）