离子交换法合成L/MCM-41复合分子筛OA北大核心CSTPCD
Synthesis of Micro/meso-porous Composite Molecular Sieve L/MCM-41 with Ion Exchange
以十六烷基三甲基溴化铵(CTAB)为模板剂,分别采用包埋法和离子交换法,两步晶化都合成了L/MCM-41复合分子筛,并通过XRD、SEM、TEM和BET等测试手段对合成样品进行表征,检测结果表明用离子交换法合成的复合分子筛孔径为3.04 nm.与水热晶化法合成的MCM-41相比:(1)壁厚由0.55 nm增大到1.81 nm；(2)水热稳定性也明显提高,在100℃沸腾状态下结构保持时间由原来的低于2h增大到8h,与L沸石相比,K+含量降低为0.26％.
Micro/meso-porous composite molecular sieve L/MCM-41 was synthesized with embedding method and ion exchange using cetyl trimethyl ammonium bromide ( CTAB ) as template and it was confirmed by being characterized by X-ray diffraction( XRD ) , scanning electron microscopy ( SEM ) , transmission electronic microscopy ( TEM ) and N2 absorption/ desorption. The results indicated that the pore diameter of L/MCM-41 composite molecular sieve was 3. 04 nm which was b…查看全部>>
卫冬燕;王春芳;陈宜俍;徐军;郭士岭;詹予忠;阎立军;潘晖华
郑州大学化工与能源学院,河南郑州450001郑州大学化工与能源学院,河南郑州450001郑州大学化工与能源学院,河南郑州450001郑州大学化工与能源学院,河南郑州450001郑州大学化工与能源学院,河南郑州450001郑州大学化工与能源学院,河南郑州450001中国石油天然气股份有限公司石油化工研究院催化材料研究室,北京100195中国石油天然气股份有限公司石油化工研究院催化材料研究室,北京100195
化学化工
离子交换介微孔复合分子筛L/MCM-41
ion exchangeMeso/micro-porous composite molecular sieveL/MCM-41
《郑州大学学报（工学版）》 2012 (1)
51-54,4
河南省基础与前沿技术研究计划资助项目(82300420090)
评论