浸渗法合金化纯钨表层的研究
Study on Infiltration Alloying of Tungsten Surface
摘要
Abstract
W-Ni-Fe alloying layer on tungsten was prepared by infiltration Ni-Fe melt. The micro-structures and the depths of alloying layer with different infiltration holding time were analyzed. Results showed that W-Ni-Fe alloying layer depths were 530μm and 700μm when the infiltration holding time was 10min and 20tnin, and the NiFe-rich phase region embedded in tungsten phase was very small. When the infiltration holding time increased to 30min and 40min, the W-Ni-Fe alloying layer depths were 750pm and 770pm, the NiFe-rich phase region significantly enlarged, and the shape of partial tungsten phase became spheroid. The forming mechanism of W-Ni-Fe alloying layer on tungsten was explained based on experimental results and W-Ni phase diagram.关键词
钨/浸渗/面向等离子体材料/合金化Key words
tungsten/ infiltration/ plasma facing materials (PFMs) /alloying分类
矿业与冶金引用本文复制引用
杨宗辉,沈以赴,孟氢钡..浸渗法合金化纯钨表层的研究[J].材料工程,2012,(7):86-91,6.基金项目
江苏省自然科学基金资助(BK2007201) （BK2007201）
江苏科技大学先进焊接技术省级重点实验室开放研究基金资助课题(JSAWT-06-02) （JSAWT-06-02）
南京工程学院校级科研基金(QKJA2009004) （QKJA2009004）