金刚石与磨料磨具工程2012，Vol.32Issue(1)：50-52,3.
镀膜金刚石膜层的俄歇分析
AES Analysis on coating of coated diamond
徐燕军 1柳成渊 2尹翔 1沈翔 2罗锡裕1
作者信息
- 1. 中国钢研科技集团有限公司,北京100081
- 2. 安泰科技股份有限公司,北京100081
- 折叠
摘要
Abstract
The coated diamonds are getting more and more important in the application of modern diamond products. In this article coatings on chrome coated and titanium coated diamonds are studied using AES . The results indicated that AES can determine the content of elements and thickness of coating accurately ; the coated diamonds all contained oxygen beside carbon, chrome and titanium, this was caused by coating surface oxidation; the thickness of chrome coating was about 25 nm and that of titanium coating was about 360 nm. XRD analysis indicated that no diffraction phase was found in the chrome coating which was too thin, while TiC-based solid solution was found in the titanium coating .关键词
镀膜金刚石/俄歇分析/镀层Key words
coated diamond/AES/coating分类
化学化工引用本文复制引用
徐燕军,柳成渊,尹翔,沈翔,罗锡裕..镀膜金刚石膜层的俄歇分析[J].金刚石与磨料磨具工程,2012,32(1):50-52,3.