塑料科技2012，Vol.40Issue(5)：96-99,4.
钛酸酯偶联剂改性Sb2O3及其性能研究
Study on Modification of Sb2O3 with Titanate Coupling Agent and Its Performance
摘要
Abstract
The Sb2O3 powder surface was organically modified with titanate coupling agent (NDZ-101). The effects of content of NDZ-101, reaction temperature and reaction time on the surface modification of Sb2O3 were researched. The modified Sb2O3 was characterized by means of FT-IR and SEM. The results show that the optimum conditions are as follows: the content of NDZ-101 is 3%, the temperature is 70℃ and the reaction time is 40 min. The surface of Sb2O3 is covered with NDZ-101 by the way of chemical grafting, and then the modified Sb2O3 powder evenly disperses into PP so as to effectively reduce the influence on the mechanical properties of PP.关键词
表面改性/钛酸酯偶联剂/氧化锑/聚丙烯/力学性能Key words
Surface modification/ Titanate coupling agent/ Sb2O3/ Polypropylene/ Mechanical properties分类
化学化工引用本文复制引用
尹作栋,苏孟,童张法,张涛,陈笑..钛酸酯偶联剂改性Sb2O3及其性能研究[J].塑料科技,2012,40(5):96-99,4.基金项目