LiFePO4锂离子电池的高倍率充放电性能OA北大核心CSCDCSTPCD
High rate charge-discharge performance of LiFePO4 Li-ion battery
研究了正极材料、正极面密度、导电剂含量及电极结构对18650型LiFePO4锂离子电池高倍率充放电性能的影响.当D50为1.92 μm,比表面积为11.4 m2/g,正极面密度为2.8 g/dm2,导电剂含量为4.0％时,电池具有较好的加工性能和倍率性能.相比于单极耳结构,双极耳结构电池的内阻减小了50％,为14 mΩ左右,且分布集中；5.00 C充电和15.00 C放电时的表面温升很小.在2.0～3.8 V充放电,优化后的20.00 C、30.…查看全部>>
The effects of cathode materials,cathode surface density,conductive agent amount and electrode structure on high rate charge-discharge performance of 18650 type LiFePO4 Li-ion battery were studied- The battery with the D50 of 1.92 fan, specific surface area of 11.4 m2/g,cathode surface density of 2.8 g/dm2 and conductive agent amount of 4.0% had better processing performance and rate capability probably. The internal resistance of battery with the stru…查看全部>>
钟海江;唐有根;卢周广;张军
中南大学化学化工学院,湖南长沙410083湖南格林新能源有限公司,湖南湘潭411101中南大学化学化工学院,湖南长沙410083中南大学化学化工学院,湖南长沙410083
信息技术与安全科学
磷酸铁锂(LiFePO4)锂离子电池高倍率充放电性能
lithium iron phosphate(LiFePO4) Li-ion battery high rate charge-discharge performance
《电池》 2012 (3)
LiFePO4的可控合成与嵌脱锂机理研究
142-145,4
国家自然科学基金(21001117)
评论